Rubber Compound

Product Description

All tire waste are selected so that only buffing is used in the process to ensure quality of Nexrubber Compound. It is quite unusual to some but Nexrubber Compound B*3 can be used **0% by itself for some rubber products.

We deal direct to tire manufacturers and perform quality check and audit of their waste before buying them.

Product Details:

Black sheet/roll - *0kg per roll
Sheet size: 3m x 0.9m x 1.5mm

Packaging - on pallet and shrink wrap.

MOQ
*0FCL : *2.5mt 
*0FCL : *2.5mt [sheet form also available to achieve *8mt/*0FCL]

Tensile strength: ****2Mpa
Mooney (1*4): *****5 [although high mooney, after blending it will reduce]
Elongation at Break : ******0%
Abrassion: *0
Hardness Shore A: *0 +/*2
Density gm/cm3: 1.*2
Tear strength N/mm: *3

Delivery: First time order ****0 days. 

Non-toxic - refer test from SIRIM.

Currently used by top tire companies to make retread for truck/bus.

How to use B*3?

1) Mix *0% B*3 in an internal mixer or two-roll with virgin/original compound *0%
2) Blend it for **5min
3) Keep temperature below **0oC
4) After blending take it out
5) Take a batch of mixed compound to a mixing mill
6) This is the same process with/without B*3. Add sulphur -same as before.
7) After **3mins - insert into an extruder
8) The output compound is ready to be mold
9) In the mold, set curing temperature for ******0oC
*0) Curing time varies between ***5mins depending on product size. Smaller product may apply fast-cure process.

Manufacturer can blend as much as possible to save cost by observing how the property drops as percentage blending increases. Manufacturer may also adjust CTP, DPG or TBBS to adjust curing time. It is worth trying and performs trial and error a bit.

Some customer blends for up to *0%. Go up step by step.

Guaranteed quality. On time delivery. 

Ordering

Deposit *0% only on order. Balance *0% before shipment and after inspection.