ORACLE TM ***0G is a *0% glass fiber reinforced
injection molding PA*6 grade for machinery components and housings
of high stiffness and dimensional stability
| TEST ITEMS | TEST METHOD AND CONDITIONS | TEST RESULTS | ||
| TEST METHOD | UNIT | CONTITIONS | ||
| (DRY)*3 | ||||
| Density | ISO***3 | g/cm3 | 1.4 | |
| Melt Volume Rate | ISO***3 | cc/*0min | (**5)2.*6kg | 9.6 |
| Tensile Strength | ISO**7 | MPa | *0mm/min | **0.4 |
| Tensile strain at break | ISO**7 | % | 5 | |
| Flexural Strength | ISO**8 | MPa | **0 | |
| Flexural Modulus | ISO**8 | MPa | 8,**0 | |
| Charpy Notched | ISO**9 | KJ/m2 | 2.9m/s*1J | *1 |
| Izod Notched Impact | ISO**0 | KJ/m2 | 3.5m/s*1J | *0.9 |
| Flame resistance | UL**4 | HB | ||
| Ash content | % | *3.5 | ||
| Processing Guidelines | ||||
| Material Handling Max. Water content: 0.*2% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at *0 °C (**6 °F) is recommended. Drying time is dependent on moisture level, but **6 hours is generally sufficient |
||||
| Typical Profile Melt Temperature ******5 °C (******1 °F) Mold Temperature ****0 °C (******4 °F) Injection and Packing Pressure *****5 bar (*******0 psi) |
||||
| Fill Rate Fast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate |
||||
ORACLE provide six series polyamides resin to serve users a wide range of needs.
>>> General Purpose Homopolymer
>>> Reinforced nylon resin(Glass-reinforced and/or Mineral-reinforced)
>>> Flame Retarded
>>> Friction&Wear resistance
>>> Impact resistance
>>> Special applications