Description
CWP is an ultra-hard, impact and abrasion resistant chrome carbide
composite alloy formed by metallurgical bonding granular chromium
carbide weld bead to steel. The result is the ultimate wear
resistant properties available for the heaviest abrasion &
impact applications. It is superior to other weld overlays on the
market.
The surface of high quality fusion cladding should always contain
distribution of large and small stress relief cracks in order to
provide maximum wear life in heavily abrasive applications. Stress
relief cracks are normal and should occur during the application of
fusion cladding to a plate. In most applications, proper layout of
the stress cracks will provide a weld overlay surface to handle
abrasives effectively and economically.
Advantages of Chrome Carbide
Can be cut, formed and welded. Pipe fabricated 2″ ID and over.Cost
effective.Stress relieved.Extended service life.Superior
abrasion/impact resistant.Good weld ability to mild steel
base.Superior to ceramics.Weld overlay can be applied to two sides
for added strength and durability Physical Properties.Carbide
Hardness****0 BHN . Chromium Carbide Matrix
Hardness**0Hrc.
Bead Width**5mm. Base Plate****5mm. Chrome Carbide Single Pass
*3mm. Chrome Carbide Double Pass *5mm.
Applications
Bucket Lips,Chipper Hoods, Chutes,Coal Chutes,Cone Liners,
Cyclones, Dozer Blades, Exhausted Blades,Fan Blades,
Fan Housings,Feeder Plates,Flop Gates,Grizzly Bars, Hoppers, Hot
Mill Guides,Liner Plates, Mining Equipment, Pipe,
Scrapers,
Shovel Liners, Skip Cars, Sluice Gates, Slurry Lines, Transitions,
Truck Liners, Vibrating Pans, Wear Plates, Whizzer Blades