WHITE HOT-MELT ROAD MARKINGS

Product Description

WHITE HOT-MELT ROAD MARKING PAINT

RAW MATERIAL COMPOSITION

Titanium oxide, Binder, Calcium Carbonate, Petroleum resin. 

Additives: Glass beads, EVA, Quartz sand.

TECHNICAL SPECIFICATION

Relative density: 1.**2.3

Softening point *****0 degrees C.

Nonsticky tire time (min) <3 

Compressive strength Mpa <*2

Glass bead content is *0%.

Heating stability ~4 hours in stirring state at **0~**0 C, without obvious yellowing, coking, caking and other phenomena. 

No wrinkles, spots, bubbles, cracks, shedding or stickiness after coating colour and appearance drying.

Life span: **5years 

PRODUCTION & TESTING STANDARDS OF HOT MELT COATINGS

China Standard JT/T *******4

Japanese Standard JISK***5

British Standards

Australian Standard 

American Standard

DOSAGE OF HOT MELT COATING

Theoretical value **0㎡/ton

PACKAGING OF HOT MELT COATING

Plastic woven bag with plastic film *5Kg/bag 

or 

Kraft paper bag *5Kg/bag

ACCESSORIES FOR HOT MELT COATING

Special primer: Select special primer for hot-melt marking paint to increase the adhesion between pavement and paint and product strength. 

Glass beads: Special glass beads for marking surface sowing are selected, with clear and transparent colour and refractive index greater than 1.5.

SUPPORTING CONSTRUCTION MACHINERY

This product is suitable for use with conventional heat-soluble road marking paint construction machinery, such as Hot-Melt Kettle, Scriber and base oil sprayer.

STORAGE

Hot-melt marking coatings are not suitable for long-term storage.